1800°C Grade MoSi2 Heating Element (40x147mm) - HEL1800T-40147

€148,19

Delivery and Shipping to EU

We will add in the quotation, the shipping, insurance, customs clearance costs.

1800°C Grade MoSi2 Heating Element (40x147mm) - HEL1800T-40147

MTI


Specifications
  • Materials: MoSi2
  • Working temperature:
    • 1750°C (in air) (shrot time)
    • 1650°C (in N2)
    • 1220°C ~ 1500°C (in H2)
  • Volume Density: 5 ~ 5.6g/cm3
  • Bend strength: 15 ~ 25kg/cm3
  • Vickers hardness: (HV) 570kg/mm2)
  • Porosity rate: 7.4%
  • Water absorption: 2%
  • Heat extensibility: 4%
Resistivity Properties of MoSi2 Heating Element
  1. The resistivity of MoSi2 heating elements rises with the increase in temperature (shown in the graph below). When the temperature of the heating stage is below 300°C, less than 35% of the total output power should be applied to avoid stressing the elements with excessive current.
  2. Generally, the resistance of heating elements will not be affected by aging under normal operating conditions, therefore old elements can be used together with new ones.
Installation When installing a heating element into furnaces, a separator should be placed between the two shanks of the heating element before hanging the element inside the furnace chamber.  The proper separator width should be selected to fit the shanks smoothly and avoid damage to the element.
Warning
Exercise extreme caution to not apply any stress on the elements during installation. Heating elements are very brittle and could break if the separator is too wide or if too much pressure is applied on them. 
No warranty will be issued for damage caused by improper installation.
Inspect your delivery:
Please check the package for damages before accepting delivery.
Should damages be found, please keep all packaging materials, take pictures, and report immediately to the carrier/MTI.
No Warranty:
Kindly note this item is a consumable part, and not covered by a warranty. Make sure to inspect for defect(s) thoroughly before use. 