0.5 mm Thick Nickel Foam for Battery Cathode Substrate or Solid-State Electrolyte Support (L 1000 x W 200 mm) - EQ-bcnf-05m

Name: 0.5 mm Thick Nickel Foam for Battery Cathode Substrate or Solid-State Electrolyte Support (L 1000 x W 200 mm) - EQ-bcnf-05m
Brand: MTI
SKU: bcnf-05m
Price: 336.88 EUR
Availability: InStock

€336,88

Delivery and Shipping to EU

We will add in the quotation, the shipping, insurance, customs clearance costs.

0.5 mm Thick Nickel Foam for Battery Cathode Substrate or Solid-State Electrolyte Support (L 1000 x W 200 mm) - EQ-bcnf-05m

MTI

Nickel Foam for Battery Cathode Substrate (1000mm length x 200mm width x 0.5 mm thickness) EQ-bcnf-05m

Specifications

Material: Nickel Foam, (excellent anti-corrosive)
Purity: > 99.9 wt %
Impurity: C?200S?80Fe?100Cu?100Si?50 ( ppm)
Surface Density: 346 g/m^2
Length: 1meter
Width: 200mm
Thickness: 0.5 mm
Net weight: 104g
Porosity: ?95% (80-110 Pores per Inch. average hole diameters about 0.25mm)
Extensibility: Lengthwise?5%; Widthwise?12%
Tensile Strength Lengthwise ?1.25N/mm^2; Widthwise?1.00N/mm^2
Sold in roll only
Notice: Please notice that it is normal to observe NiO peaks in the nickel foam in XRD data. It is really difficult to avoid the oxidation of nickel.
How to clean the Nickel Foam for Battery Cathode Substrate.

It can be removed the NiO by annealing in the hydrogen furnace.
Nickel foam (about 3.3 cm x 1 cm) was carefully cleaned with the concentrated HCl solution (37 wt.%) in an ultrasound bath for 5 min in order to remove the surface oxide layer. And then deionized water and absolute ethanol was used for 5 min each to ensure the surface of the Ni foam was well cleaned.