MTI  |  SKU: Lib-LNCM811-SC

Single Crystal Powder: LiNiCoMnO2 (Ni:Co:Mn=8:1:1) Powder for Li-ion Battery Cathode, 200g/bottle - Lib-LNCM811-SC

€472,18

Delivery and Shipping to EU

We will add in the quotation, the shipping, insurance, customs clearance costs.

Single Crystal Powder: LiNiCoMnO2 (Ni:Co:Mn=8:1:1) Powder for Li-ion Battery Cathode, 200g/bottle - Lib-LNCM811-SC

MTI

Single Crystal LiNiCoMnO2 (Lithium Nickel Manganese Cobalt Oxide, Ni:Co:Mn=8:1:1) withan electrochemomechanically compliant microstructures has attracted great attention in Li-ion battery for its superior electrochemical performance compared to the polycrystalline counterpart

Specification
Properties Item Standard Value Typical Value

Chemical Composition 		Ni (mol%) 83.0 ± 0.5 82.8%
Co (mol%) 11.0 ± 0.5 10.9%
Mn (mol%) 6.0 ± 0.5 6.2%

Size Distribution

 D10 (?m) ? 1.8  2.4
D50 (?m) 4.0±0.5 4.4
D90 (?m) ? 14 11.6
Specific Surface Area (m2/g)
 BET 0.70 ± 0.15
 0.79
Tap Density (g/cm³) ? 1.8 2.22
Moisture (ppm) ? 500 281
pH
 11.0 ± 0.50 11.44
Residual

Li2CO3 (wt%)

 ? 0.20 0.177
LiOH (wt%) ? 0.25
 0.150
Li (ppm) ? 7.30 7.39

Impurities 		Fe (ppm) ? 50 21
Cu (ppm) ? 20 2
Na (ppm) ? 350 13
S (ppm) ? 2500 260
 
Specific Capacity (3.0-4.25 V) (mAh/g) 		0.3 C   195.8
1 C 185.6

Note		 MTI does not manufacture this product, and only sell the small quantity to research for development for new generation battery. If you need a larger quantity or have a question for IP, we will forward your inquiry to the producer.


Application Notes:
  1. Please click to see Procedure for Preparing Anode & Cathode Electrode Slurry.
  2. Please keep the powder in the vacuum box to avoid moisture.
  3. Please bake the powder in a vacuum oven at 120 - 150 °C before making slurry and coating to ensure max. capacity.
  4. The product is for research only, not supply for large quantity, 

Related Products

Vacuum Storage Box		 laboratory mill and mixer    
Powder Milling & Mixer 		 
Electrode Coaters
Battery Research Equipment
Other Battery Powder
Solid Electrolyte
Back to top