Li-Ion Battery Cathode - Aluminum Foil Double Side Coated by Li-NCM (6:2:2 ) (241mm L x 200mm W x 0.1mm T) 5 sheets/bag - bc-af-241NCM-DS622

This electrode sheet is based on Aluminum foil coated by Lithium Nickel Manganese Cobalt Oxide (NCM622) on double sides and can be used as the cathode of Li-Ion battery -- 5 sheets /bag

SPECIFICATIONS

• Material:  LiNiCoMnO2  6:2:2)
• Current collector (substrate): Aluminum foil (16 microns, area desnityof 4.22mg/cm2)
• Coated Area: 241mm L x 175mm W. The edge width of blank area is 12.5 mm for each side.  
• Double sides area density: 22 ± 0.4 mg/cm2
• Compaction density: 3.3 ± 0.1 g/cm2
• Coating Thickness: ~67 um
• Total Thickness: ~83 um
• Active Material Weight: 9.05 g
• Active Material Proportion in Powder: 97.5% 
• Specific Capacity: 170 mAh/g [0.1C, 3.0-4.3 V vs Li/Li+, Half Cell] [Electrolyte:1.0M LiPF6 in EC:DMC:EMC=1:1:1 Vol% with 1.0%VC]
• Note:  The electrode sheet shall be stored in a vacuum box, a vacuum oven or a glove box to avoid degradation.

•  for NCM
•  for Aluminum

Please click the video below to see how MTI's slitting machine prepares electrode of cylinder batteries

Please click the video below to see how MTI's MSK-T-10 disc and ring cutter to cut electrode sheet

                     

Related Products:

Other Li-ion Battery Electrode

Vacuum Storage Box & Oven

Vacuum Drying/Bake-out Ovens

Coin Cell Assembling

Pouch Cell Assembling

Cylindrical Cell Assembling

Battery Testing